Transmission electron microscopy study of defect reduction in two-step lateral epitaxial overgrown nonplanar GaN substrate templates
Transmission electron microscopy (TEM) is carried out to characterize the extended defect reduction in low-defect nonplanar GaN substrate templates grown by lateral epitaxial overgrowth (LEO). The LEO nonplanar GaN substrate template has a trapezoidal cross section with smooth (0 0 0 1) and {1122} facets. We demonstrate here the dislocation distribution and behavior in both ordinary LEO and two-step LEO. Penetration of threading dislocations (TDs) beyond mask windows is observed in ordinary LEO substrates. In two-step LEO substrates, which utilize the tendency for TDs to bend 90° at certain plane interfaces, only a type dislocations with Burgers vector b=1/3(1120)are generated in the upper part above the TD bending zone between two mask windows with a density of ∼8×107 cm−2, and there are almost no dislocations in the LEO wing region. This approach provides a promising path to produce low-defect GaN substrate templates for high-performance buried heterostructure lasers.
Source: Journal of Crystal Growth
If you need more information about Transmission electron microscopy study of defect reduction in two-step lateral epitaxial overgrown nonplanar GaN substrate templates,please visit:http://www.qualitymaterial.net/ or send us email at sales@qualitymaterial.net.